Synthesis of high impact polystyrene: the eff ect of butadiene rubber molecular parameters
https://doi.org/10.35164/0554-2901-2019-5-6-20-23
Abstract
The eff ect of butadiene rubber molecular parameters on conversion dependencies and viscosity characteristics of the process of graft copolymerization of styrene, microstructure and quality indicators of the synthesized samples of impact-resistant polystyrene was studied. It is testifi ed that an increase in the molecular mass of the elastomer does not aff ect the monomer conversion, however, it leads to a phase inversion shifting to the region of lower conversion degrees of styrene. In this case, an increase in the size of rubber particles and an increase in the content of the gel fraction are observed in the copolymer. The established changes in the microstructure correlate with the properties of high-impact polystyrene.
About the Authors
E. N. Tkacheva
PJSC Nizhnekamskneftekhim
Russian Federation
City of Nizhnekamsk
Russian Federation
City of Nizhnekamsk
O. M. Trifonova
PJSC Nizhnekamskneftekhim
Russian Federation
City of Nizhnekamsk
Russian Federation
City of Nizhnekamsk
I. G. Akhmetov
PJSC Nizhnekamskneftekhim
Russian Federation
City of Nizhnekamsk
Russian Federation
City of Nizhnekamsk
References
1. Полистирол в России -2018. Ежегодный обзор. URL: http://www.mrcplast.ru/
2. Ткачева, Е.Н. Химически стойкий ударопрочный полистирол, предпосылки создания производства в РФ / Ткачева Е.Н., Трифонова О.М., Ахметов И.Г. // Пластические массы. -2018. -№ 5-6. -С.61-64.
3. Ткачева, Е.Н. Изучение свойств, состава и структуры полистиролов, стойких к растрескиванию под воздействием окружающей среды / Ткачева Е.Н., Трифонова О.М., Ахметов И.Г. // Пластические массы. -2019. -№ 1-2. -С.9-12.
4. Pat.3243481 US, Int/ Cl.7 C08F2/02. Process for making graft copolymers of vinil aromatic compounds and stereospecifi c rubbers / Norman R. Ruffi ng, Bernie A. Kozakiewicz [e tc.]; Dow Chemical Company. № 164,728 08.01.1962; date of hatent 29.03.1966.20 p.
5. Seong, J. LEE. The evolution of the size distribution of rubber particles over time during the mass polymerization of high-impact polystyrene / Journal of Chemical Engineering of Japan. -2004. -Vol. 37. № 2. Р. 217-223.
6. The infl uence of small rubber particles on the resistance to cracking of impact polystyrene under the action of stresses in aggressive environments. URL: http://www.wileyonlinelibrary.com/
7. Рязанцев, В.И. Блок-сополимеры стирола с каучуками / Рязанцев В.И, Минскер К.С, Дановская Е.Е // Пластические массы. -1976. -№ 7. -С.64-65.
8. Echte, A. Teilchenbildung bei der Herstellung von kautschukmodifi ziertem Polystyrol / Die Angewandte Makromolekulare Chemie 58/59.-1977.Nr. 846. Р. 175 198.
9. ASTM D 1646-17. Стандартные методы испытания каучуков – определение вязкости, релаксации напряжения и характеристик подвулканизации с использованием вискозиметра Муни, 2005. -39 с.
10. Коротнева, Л.А. Каучуки, применяемые в производстве ударопрочных сополимеров стирола / НИИТЭХИМ. -М., 1979. -23 с.
11. Егорова, Е.И. Основы технологии полистирольных пластиков / Егорова Е.И., Коптенармусов В.Б. – СПб.: Химиздат, 2005. – 300 с.
12. Бакнелл, К.Б. Ударопрочные пластики / К.Б.Бакнелл; пер. с англ. под ред. Лишанского И.С. -Л.: Химия, 1981. -328 с.
13. Пат. 2222554 Российская федерация, МПК7 С08L 25/06. Флонстойкая композиция модифицированного каучуком полистирола / Ковано Кодзи, Мацуба Кенитиро; заявитель и патентообладатель Toyo Engineering Corporation. -№ 20011286501/04; заявл. 23.10.2001; опубл. 20.06.2003, Бюл. № 3. -12 с.
14. Баллова, Г.Д. Влияние показателей бутадиенового каучука на прививочную сополимеризацию стирола / Баллова Г.Д. Вылегжанина К.А. Егорова Е.И. и др. // Пластические массы. -1972. -№ 7. -С.52-54.
Review
For citations:
Tkacheva E.N., Trifonova O.M., Akhmetov I.G. Synthesis of high impact polystyrene: the eff ect of butadiene rubber molecular parameters. Plasticheskie massy. 2019;(5-6):20-23. (In Russ.) https://doi.org/10.35164/0554-2901-2019-5-6-20-23
Views:
779
Email this article 