Properties, structure and composition of environmental stress cracking resistance polystyrenes
Abstract
High-impact extended study has been performed for commercial specimens of various manufacturers announced their products as having environmental stress crack resistance (ESCR HIPS). The specimens under the study revealed their chemical resistance to be within the wide range, practically from 12 to 88 %. Besides, physical and mechanical properties, structural parameters and composition of ESCR HIPS were compared to the chemical resistance ratio. Electronic microscopy was found to be as the most informative method of structural analysis enabling to reveal differences in the studied specimens.
About the Authors
E. N. Tkacheva
PJSC Nizhnekamskneftekhim
Russian Federation
Russian Federation
O. M. Trifonova
PJSC Nizhnekamskneftekhim
Russian Federation
Russian Federation
I. G. Akhmetov
PJSC Nizhnekamskneftekhim
Russian Federation
Russian Federation
References
1. Полистирол в России - 2018. Ежегодный обзор. URL: http:// www. mrcplast.ru/
2. Ткачева, Е.Н. Химически стойкий ударопрочный полистирол, предпосылки создания производства в РФ / Ткачева Е.Н, Трифонова О.М, Ахметов И.Г // Пластические массы.-2018.- № 5-6.-С.61-64.
3. Xiangyang, Li. Environmental Stress Cracking Resistance of a New Copolymer of Bisphenol / Xiangyang, Li // A. Polymer Degradation and Stability. -2005.-Vol. 90. № 1. Р. 44-52.
4. Pat. 4144204 Germany, Int/ Cl.7 C08L 7/00. Impact-resistant thermoplastic molding composition with increased stress crack resistance / Hans Mittnacht, Adolf Echte, Helmut Jenne [e tc.]; BASF Aktiengesellschaft.- № 686,367 14.05.1976; date of hatent 13.03.1979.- 10 p.
5. Ахсанова, О.Л. Атомно - эмиссионное определение цинка в полистироле / Ахсанова О.Л, Загитов Р.М., Трифонова О.М // Заводская лаборатория. Диагностика материалов.-2016.-Т. 82. № 4. С. 22-25.
6. Егорова, Е.И. Основы технологии полистирольных пластиков / Егорова Е.И., Коптенармусов В.Б. - СПб.: Химиздат, 2005. - 300 с.
7. Pat.3243481 US, Int/ Cl.7 C08F2/02. Process for making graft cjpolymers of vinil aromatic compounds and stereospecific rubbers / Norman R. Ruffing, Bernie A. Kozakiewicz [e tc.]; Dow Chemical Company.- № 164,728 08.01.1962; date of hatent 29.03.1966.- 20 p.
8. Seong ,J. LEE. The evolution of the size distribution of rubber particles over time during the mass polymerization of high-impact polystyrene / Journal of Chemical Engineering of Japan.-2004.- Vol. 37. № 2. Р. 217 - 223.
9. The influence of small rubber particles on the resistance to cracking of impact polystyrene under the action of stresses in aggressive environments. URL: http:// www.wileyonlinelibrary.com /
10. ASTM D 5296-05. Стандартный метод испытаний для определения средней молекулярной массы и молекулярно-массового распределения полистирола методом высокоэффективной эксклюзионной хроматографии; 2005.- 44 с.
11. Пат. 2222554 Российская федерация, МПК7 С08L 25/06. Флонстойкая композиция модифицированного каучуком полистирола / Ковано Кодзи, Мацуба Кенитиро; заявитель и патентообладатель Toyo Engineering Corporation.- № 20011286501/04; заявл. 23.10.2001; опубл. 20.06.2003, Бюл. № 3.-12 с.
12. WO 2012/0059110 US, Int/ Cl. C08L 21/00. Refrigerator lining / Michel Duc, Jan Neelen [e tc.]; Total Petrochemicals Research Feluy.- № 13/203,886 09.03.2010; publ. 08.03.2012.- 12 p.
13. Буряк, В.П. Мировой рынок полистиролов / Буряк В.П // Полимерные материалы.-2004.-№ 10.-С.10-14.
14. Echte, A. Rubber Toughened Polymers / Echte A // BASF, Review ACS Series. -1989.- 49 р.
Review
For citations:
Tkacheva E.N., Trifonova O.M., Akhmetov I.G. Properties, structure and composition of environmental stress cracking resistance polystyrenes. Plasticheskie massy. 2019;(1-2):9-12. (In Russ.)
Views:
430
Email this article 