Investigation of the mechanical properties of films from a mixture of HDPE with LLDPE with the addition of chalk concentrate
https://doi.org/10.35164/0554-2901-2023-1-2-35-38
Abstract
The deformation-strength characteristics of films made from a mixture of HDPE and LLDPE modified with chalk were studied. It is shown that the introduction of a chalk concentrate of more than 16 wt.% (the content of chalk concentrate is 20 wt.%) has a negative effect on the strength and relative elongation at break of the composition of HDPE with LLDPE, as well as on the strength of the welded joint of polymer films. The strength of the films in the longitudinal and transverse directions significantly depends on the composition of the composition. The strength of the weld, obtained by ultrasonic welding, decreases sharply when the chalk content in the system is more than 16 wt.%. The introduction of more than 10 wt.% LLDPE into a HDPE-based chalk-filled composition is inadvisable..
About the Authors
O. I. Abramushkina
MIREA - Russian Technological University (Institute of Fine Chemical Technologies named after M.V. Lomonosov)
Russian Federation
Russian Federation
Moscow
E. A. Romakhova
Federal State Autonomous Educational Institution of Higher Education “Moscow Polytechnic University”
Russian Federation
Russian Federation
Moscow
I. N. Tsapenko
JSC “Interindustry Institute of Plastics Processing – NPO “Plastic”
Russian Federation
Russian Federation
Moscow
References
1. Колгрюбер К. Двухшнековые сонаправленные экструдеры. Основы, технология, применение/Колгрюбер К., под ред. Узденского В.Б.//С-Пб.: ЦОП Профессия, 2016.
2. Шиллер М. Добавки к ПВХ. Состав, свойства, применение/ Шиллер М. под ред. Тихонова Н.Н. // С-Пб.: ЦОП Профессия. – 2017. – 400 с., с. 72–73, с. 149.
3. Дудочкина Е.А. Канд. дисс. Закономерности формирования структурно-механических свойств высоконаполненных полиолефиновых композиций – М. – 2019 – URL: https://diss.muctr.ru/media/dissertations/2019/03/%D0%94%D0%B8%D1%81%D1%81%D0%B5%D1%80%D1%82%D0%B0%D1%86%D0%B8%D1%8F_%D0%98%D0%A2%D0%9E%D0%93.pdf].
4. Абзальдинов Х.С. Адгезионные свойства композиций на основе низкомолекулярных полиолефинов / Абзальдинов Х.С., Садова А.Н., Яруллин Р.С.// Вестник Казанского технологического университета, т.16, №23, 2013 – с. 87-89 URL: https://cyberleninka.ru/article/n/adgezionnye-svoystva-kompozitsiy-na-osnovenizkomolekulyarnyh-poliolefinov.
5. Волков С.С. Влияние наполнителей и красителей на качество сварных соединений при ультразвуковой сварке / Волков С.С., Коновалов А.В., Ремизов А.Л.// Известия высших учебных заведений. Машиностроение. – 2020. – №1. – С. 13–20. URL: http://izvuzmash.ru/catal…l/weld_rel/1725.html.
6. Мяленко Д.М., Михайленко П.Г. Исследования изменения физико-механических характеристик полимерных пленочных материалов на основе полиэтилена, наполненных СаСО3, при воздействии ультрафиолетового излучения. URL: https://cyberleninka.ru/article/n/issledovaniya-izmeneniya-fiziko-mehanicheskih-harakteristik-polimernyh-plenochnyh-materialov-na-osnove-polietilena-napolnennyh.
7. Милевски Дж. Наполнители для полимерных композиционных материалов : справ. пособие / Милевски Дж., Кац Г., Ферригно Т.Х. и др. ; под ред. П.Г. Бабаевского // М.: Химия. – 1981. – С. 138–139.
Review
For citations:
Abramushkina O.I., Romakhova E.A., Tsapenko I.N. Investigation of the mechanical properties of films from a mixture of HDPE with LLDPE with the addition of chalk concentrate. Plasticheskie massy. 2023;1(1-2):35-38. (In Russ.) https://doi.org/10.35164/0554-2901-2023-1-2-35-38
Views:
216
Email this article 