Investigation of the curing process of epoxy compositions by developed amine products based on household waste polyethylene terephthalate and polycarbonate

The objects of research are oligomers-hardeners obtained by aminolysis of secondary polyethylene terephthalate (PET) and polycarbonate (PC) household waste with an aliphatic amine (PEP).

The epoxy-diane resin of the ED-20 brand was chosen as the binder cured by the obtained oligomers due to its availability, good properties, acceptable viscosity, and wide applicability. The study of some parameters of the curing of thermosetting resin by industrial and synthesized hardeners is carried out.

The gelation times at elevated temperatures (in the range from 50 to 100°C) and the activation energies of epoxy compositions were determined, and the conversion of epoxy groups during curing at room temperature was studied. The analysis of the obtained data showed that the structural features of macromolecules caused by the introduction of PET and PC fragments have a negligible effect on the activation energy and affect only when cured at room temperature and increase the viability of the compositions, while the gelation time at elevated temperatures in the case of all the studied hardeners is almost the same.

1. Мошинский, Л. Эпоксидные смолы и отвердители / Л. Мошинский. - Тель-Авив: Аркадия пресс Лтд, 1995. - 370 с.

2. Пластмассы со специальными свойствами. Сборник научных трудов / Под общей редакцией Н.А. Лаврова - СПб.: Профессия, 2011. - 344 с.

3. Николаев А.Ф., Крыжановский В.К., Бурлов В.В., Шульгина Э.С., Лавров Н.А., Дворко И.М., Сивцов Е.В., Крыжановская Ю.В., Семенова А.Д. Технология полимерных материалов/. - СПб.: Профессия, 2011. - 544 с.

4. Воронков, А.Г. Эпоксидные полимеррастворы для ремонта и защиты строительных изделий и конструкций: учебное пособие / А.Г. Воронков, В.П. Ярцев. - Тамбов: Изд-во Тамб. гос. техн. ун-та, 2006. - 92 с.

5. Ла Мантия Ф. Вторичная переработка пластмасс - СПб.: Профессия, 2007. - 400 с.

6. Панфилов Д.А., Дворко И.М., Аликин М.Б., Литосов ГЭ. Применение отходов полиэтилентерефталата для получения пенофенопластов конструкционного назначения // Все материалы. Энциклопедический справочник с Приложением «Комментарии к стандартам, ТУ, сертификатам». - 2016. - №10. - С. 34-37.

7. Панфилов Д.А., Дворко И.М. Пеноматериалы конструкционного назначения на основе новолачных композиций, модифицированных олигоэфирами // Пласт. массы. - 2014. - № 1-2. - С. 51-53.

8. Панфилов Д.А., Дворко И.М. Пенополиуретаны на основе олигоэфирных продуктов деструкции вторичного полиэтилен-терефталата // Естественные и технические науки. - М.: Спутник+. - 2014. - №5 (73). - С. 179-183.

9. Panfilov D.A., Dvorko I.M. The Effect of Oligoethers Based on Secondary Polyethylene Terephthalate and Oligopropylene Diol on the Properties of Novolac Compounds // Polymer Science, Series D. - 2018. - Vol. 11, №2. - P. 169-173.

10. Аликин М.Б., Панфилов Д.А., Лавров Н.А., Дворко И.М. Получение ненасыщенных полиэфирных смол и материалов на их основе с использованием вторичного полиэтилентерефталата // Пласт. массы. - 2019. - №9-10. - С. 20-22.

11. Alekseeva K.D. Determination of the structure of the substance synthesized based on polycarbonate and aliphatic polyamine // "Chemistry of Organoelement Compounds and Polymers 2019". -M.: INEOS RAS, 2019. - P. 269.

12. Аликин М.Б., Шаботина О.О., Панфилов Д.А. Перспективные способы использования вторичного полиэтилентерефталата в технологии конструкционных полимерных материалов // Современные проблемы экологии: доклады XXII междунар. науч.-практич. конференции под общ. ред. В.М. Панарина. -Тула: Инновационные технологии, 2019. - С. 16-19.

13. ГОСТ Р 57779-2017. Пластмассы. Смолы фенольные. Определение времени гелеобразования на полимеризационной плитке : национальный стандарт Российской Федерации : издание официальное : введен впервые: дата введения 2018-06-01. -Москва: Стандартинформ, 2017. - 4 с.

14. ГОСТ Р 57941-2017. Композиты полимерные. Инфракрасная спектроскопия. Качественный анализ: национальный стандарт Российской Федерации : издание официальное : введен впервые : дата введения 2018-06- 01. - Москва: Стандартинформ, 2017. - 24 с.

15. ГОСТ Р 57939-2017. Композиты полимерные. Инфракрасная спектроскопия. Общие принципы : национальный стандарт Российской Федерации: издание официальное : введен впервые : дата введения 2018-06-01. - Москва: Стандартинформ, 2017. - 20 с.