Development of effective compositions of composite wood-plastic board materials based on local raw materials and industrial waste

The article presents the results of research aimed at creating of effective compositions of composite wood-plastic board materials based on fillers from cotton stalks and polymer binders.
IIt was found that for all the considered plates with a density of 600, 700 and 800 kg/m3, the maximum value of the bending strength of composite wood-plastic materials (14.8–22.9 MPa) is observed when the content of small particles of the crushed mass of cotton stems is from 10 to 20%, and the maximum value of the tensile strength perpendicular to the plate layer (0.58–0.91 MPa) – at the content of a fine fraction from 15 to 25%. The minimum water absorption of plates at three densities of 650, 750 and 850 kg / cm3 was recorded with a fine fraction content of 15–18% in the mass.
It was revealed that the high value of the ultimate strength in static bending of composite wood-plastic materials with a density of 650, 750 and 850 kg/cm3 with a content of the fibrous part of cotton 20-60% is in the range of 14-15,5 MPa, 17,5-19,1 MPa and 20-22,2 MPa, respectively. The least water absorption and swelling of the slabs is observed when the content of the fibrous part is in the range of 30-40%.

composition, wood-plastic board, cotton stalks, polymer binders, flowability, fine and fibrous particles, wood fraction, density, modulus of elasticity, resistivity

1. Бурный рост производства древесностружечных и вафельных плит. Ctryrik B // North Joqqer and Timber Process. – 1984. vol. 32. №9. P. 8-9.

2. Карасев Е.И. Развитие производства древесных плит. Уч. пособие для вузов.-- М.: МГУЛ. 2001. - с. 3-10, 89-93.

3. Суровцева Л.С. Технология и оборудование производства композиционных древесных материалов. Учебник для вузов. Издательство Архангельского гос. техн. ун-та, 2001. - с. 3-7, 180-210.

4. Deppe H.J., Ernst К. MDF - mitteldichte Faserplatten. DRW-Verlag. 1996. р. 10-21, 102-120.

5. Deppe H.J., Ernst K. Taschenbuch der Spanplattentechnik (4. Auflage). DRW-Verlag, Stutgart, BRD. 2000. р. 5-10, 112-164.

6. European Panel Federation (EPF). Annual Report. 2001-2002. p. 3-6, 282-311.

7. Брайтенбах П. Установка для непрерывного производства плит из богассы. - Рекламный проспект фирмы "Бизон-Ворд" Ультра-ворд /Группа "Афкол", Мэйлейн, Южная Африка, 1990. С 1-3.

8. Brikmon "Banmrwollsten-Rostoll Sur Vondie Spanuplaten" Bisonwerke Bahke and Jreten. 1979. C 10-14.

9. Christensen F.J., Christensen M.L. The production of hardboard from bagasse and cresol resin. Commonwealth scientific and cendustrual research organization, south Melbourne. – Australia. - 1955. - 18 p.

10. Завражнов A.M. и др. Лесопользование отходов, переработка однолетних растений в качестве сырья для изготовления плитных материалов //Совершенствование технологии и оборудования для производства древесных плит. - Сб. трудов ШЛО «Союзнаучплитпром» ВНЛДрев. Балабаново, 1983.- с. 54-606.

11. Мезенцев А.В. Разработка метода и технологии изготовления плитных материалов из одревесневших остатков однолетних растений без добавления связующих.  Автореферат канд. дис. - Свердловск, 1973, С. 5-12.

12. Верес В.Ф. Сырье для древесных плит из местных ресурсов // Деревообрабатывающая промышленность, 1962. - №9. - с.19-20.

13. Голубицкая Г.А. Некоторые свойства стеблей хлопчатника и некоторые физико-механические показатели строительных пластиков из частиц хлопковых стеблей //Тезисы докл. ХVI научной конференции Аз ПЛ. - Баку, 1967. - с. 22.

14. Use of aqricultural and industrial wasters in low – cost construction/ - New York, - 1977. 127 p.

15. Miller H.A. Particle board manufacture, Park Ridge New Jersey, Nayes Date Corporation. 1977. – p. 112-124.

16. Moslemi A.A. Particleboard: Materials, Illinоis, Southern Jllinois University Press. – 1974. – p. 112-142.

17. Special issue on agricultural waste utilization/ Small industry journal Qivzon City. Philippiness. - 1976. р. 9-11.

18. Кудилов В., Петров П. Все резервы - в дело //Хлопководство. Агропромиздат, 1985, № 4, 12-14.

19. Система получения электричества и пара из хлопковой шелухи // Oil mill garetter. - 1985, vol. 89. №10. р. 14-16.

20. Ерматов И. Использование отходов хлопководства // Хлопководство. - 1986, №4, с.10-11.

21. Ерматов Л.Т., Абдуллаев А. Отходы хлопководства в дело // Сельское хозяйство Узбекистана. - 1985, № 10, с. 13-14.

22. Неринский А.С. Ерматов Л.Т. Об оценке отходов производства хлопка //Планирование и учет в с/х предприятиях. - 1985, №2, с. 32-35.

23. Бумага из гуза-паи //Ташкентская правда. - 4 сентября, 1981, 2 с.

24. Авторское свидетельство. №114952 СССР, МКИ В27 11/06. 1984 Устройство для измельчения стеблей растения в тюках. Негматов С.С., Саидов М.М., Атаходжаев А. 25. Негматов С.С., Холмуродова Д.К., Абед Ш.Ж., Буриев Н.И., Аскаров К.А., Саидов М.М., Атаходжаев Л., Абдуллаев М.Б. Технология получения наполнителей из стеблей хлопчатника для производства композиционных древесно-пластиковых материалов. Ташкент, ГУП «Фан ва тараккиёт», 2010 г., 24 с.

25. Негматов С.С., Саидов М.М., Туляганов Б.Х., Холмуродова Д.К., Лысенко А.М., Абдуллаев М.Б., Мухитдинов З.Н. Технология

26. получения наполнителя из стеблей хлопчатника для производства композиционных древесно-пластиковых материалов. РНТК Новые композиционные материалы на основе органических и неорганических ингредиентов. 27-28 сентября 2012 г., 30-2 с.

27. Холмуродова Д.К., Негматов С.С., Саидов М.М., Туляганов Б.Х. Факторы, влияющие на формирование и величину физико-механических свойств композиционных древесно-пластиковых материалов и плит. РНТК Композиционные материалы на основе техногенных отходов и местного сырья: состав, свойства и применение» 15-16 апреля 2010 г. – с. 23-25.

28. Холмуродова Д.К., Негматов С.С., Лысенко А.М., Саидов М.М., Туляганов Б.Х., Мухитдинов З.Н. Методика определения физико-механических свойств композиционных древесно- пластиковых плитных материалов. МНТК Новые композиционные материалы на основе местного и вторичного сырья. 5-7 мая 2011 г. – С. 68-70.

29. Холмуродова Д.К., Негматов С.С., Лысенко А.М., Саидов М.М., Туляганов Б.Х., Мухитдинов З.Н. Методика обработки результатов измерений физико-механических свойств композиционных древесно-пластиковых плитных материалов. МНТК Новые композиционные материалы на основе местного и вторичного сырья. 5-7 мая 2011 г. – С.29-30.