plasticnewsПластические массыPlasticheskie massy0554-2901PLASTMASSY Publishing House (Moscow)10.35164/0554-2901-2023-11-12-21-25plasticnews-933Research ArticleСТРУКТУРА И СВОЙСТВАSTRUCTURE AND PROPERTIESТермостойкость огнезащитных материалов на основе ПВХ-пластикатов различного составаThermal stability of fire-retardant materials based on PVC compounds of various compositionsГалигузовА. А.GaliguzovA. A.

Москва, Подольск

Moscow 

agaliguzov@yandex.ruЯшинН. В.YashinN. V.

Москва

Moscow 

АвдеевВ. В.AvdeevV. V.

Москва

Moscow 

МГУ имени М.В. Ломоносова; АО УНИХИМТЕК, МОРоссияLomonosov Moscow State University; UNICHIMTEK JSCRussian FederationМГУ имени М.В. ЛомоносоваРоссияLomonosov Moscow State UniversityRussian Federation202311012024011-122125Copyright © Галигузов А.А., Яшин Н.В., Авдеев В.В., 20242024Галигузов А.А., Яшин Н.В., Авдеев В.В.Galiguzov A.A., Yashin N.V., Avdeev V.V.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://www.plastics-news.ru/jour/article/view/933

В работе представлены результаты исследования влияния состава ПВХ-пластиката на термостойкость огнезащитных материалов на его основе. Исследование проведено на примере суспензионных марок ПВХ различной молекулярной массы и с различным содержанием пластификатора. В результате было показано, что на термостойкость огнезащитных материалов, наполненных окисленным графитом, значительное влияние оказывает как содержание пластификатора, так и молекулярная масса ПВХ. Также существует зависимость изменения термостойкости огнезащитных материалов от вязкости полимерной матрицы.

The paper presents the results of a study of the effect of the composition of PVC compound on the heat resistance of fire-retardant materials based on it. The study was carried out on the example of PVC suspension grades of different molecular weight and with different content of the plasticizer. As a result, it was shown that the heat resistance of fire-retardant materials filled with oxidized graphite is significantly affected by both the content of the plasticizer and the molecular weight of PVC. There is also a dependence of the change in the heat resistance of fire-retardant materials on the viscosity of the polymer matrix.

поливинилхлоридпластификаторокисленный графитинтумесцентный материалогнезащитный материалкомпаундированиеэкструзиятермостойкостьpolyvinylchlorideplasticizeroxidized graphiteintumescent materialfire-retardant materialcompoundingextrusionthermal stabilityReferencesPrice D., Horroks A.R. Fire Retardancy of Polymeric Materials. In Fire Retardancy of Polymeric Materials. Ed. by Wilkie C.A., Morgan A.B. - Taylor and Francis. - Boca Raton, 2010. – P. 35–36.Price D., Horroks A.R. Fire Retardancy of Polymeric Materials. In Fire Retardancy of Polymeric Materials. Ed. by Wilkie C.A., Morgan A.B. - Taylor and Francis. - Boca Raton, 2010. – P. 35–36.Qu H., Wu W., Xie J., Xu J. A novel intumescent flame retardant and smoke suppression system for fl exible PVC // Polymers for Advanced Technologies. – 2011. – №22. – P. 1174–1181.Qu H., Wu W., Xie J., Xu J. A novel intumescent flame retardant and smoke suppression system for fl exible PVC // Polymers for Advanced Technologies. – 2011. – №22. – P. 1174–1181.Focke W.W., Muiambo H., Mhike W. Flexible PVC flame retarded with expandable graphite // Polymer Degradation and Stability. – 2014. – №100. – P. 63–69.Focke W.W., Muiambo H., Mhike W. Flexible PVC flame retarded with expandable graphite // Polymer Degradation and Stability. – 2014. – №100. – P. 63–69.Халтуринский Н.А., Новиков Д.Д., Жорина Л.А., Компаниец Л.В., Рудакова Т.А. Влияние интумесцентных антипиренов на горючесть ПВХ пластикатов // Химическая физика и мезоскопия. – 2009. – Т.11. – №1. – С. 22–27.Халтуринский Н.А., Новиков Д.Д., Жорина Л.А., Компаниец Л.В., Рудакова Т.А. Влияние интумесцентных антипиренов на горючесть ПВХ пластикатов // Химическая физика и мезоскопия. – 2009. – Т.11. – №1. – С. 22–27.Архангельский И.В., Годунов И.А., Яшин Н.В., Нагановский Ю.К., Шорникова О.Н. Кинетика вспенивания терморасширяющихся огнезащитных составов // Пожаровзрывобезопасность. – 2020. – Т.29. – №5. – С. 71–78.Архангельский И.В., Годунов И.А., Яшин Н.В., Нагановский Ю.К., Шорникова О.Н. Кинетика вспенивания терморасширяющихся огнезащитных составов // Пожаровзрывобезопасность. – 2020. – Т.29. – №5. – С. 71–78.Фиалков А.С. Углерод, межслоевые соединения и композиты на его основе. – М.: Аспект Пресс. – 1997. – С. 365.Фиалков А.С. Углерод, межслоевые соединения и композиты на его основе. – М.: Аспект Пресс. – 1997. – С. 365.Zybina O., Gravit M. Intumescent Coatings for Fire Protection of Building Structures and Materials. – Springer. – 2020. – 221 p.Zybina O., Gravit M. Intumescent Coatings for Fire Protection of Building Structures and Materials. – Springer. – 2020. – 221 p.Zheng Z., Liu Y., Zhang L., Wang H. Synergistic effect of expandable graphite and intumescent flame retardants on the flame retardancy and thermal stability of polypropylene // Journal of Materials Science. – 2016. – №51. – P. 5857–5871.Zheng Z., Liu Y., Zhang L., Wang H. Synergistic effect of expandable graphite and intumescent flame retardants on the flame retardancy and thermal stability of polypropylene // Journal of Materials Science. – 2016. – №51. – P. 5857–5871.Cheng Z., Liao D., Hu X., Li W., Xie C., Zhang H., Yang W. Synergistic fi re retardant effect between expandable graphite and ferrocene-based non-phosphorus polymer on polypropylene // Polymer Degradation and Stability. – 2020. – №178. – P. 109201.Cheng Z., Liao D., Hu X., Li W., Xie C., Zhang H., Yang W. Synergistic fi re retardant effect between expandable graphite and ferrocene-based non-phosphorus polymer on polypropylene // Polymer Degradation and Stability. – 2020. – №178. – P. 109201.Liang S., Liu J., Guo Y., Luo J., Liu H., Peng S. Role of expandable graphite on flame retardancy, smoke suppression, and acid resistance of polypropylene/magnesium hydroxide composites // Polymer Engineering and Science. – 2022. – №62. – P. 3168–3179.Liang S., Liu J., Guo Y., Luo J., Liu H., Peng S. Role of expandable graphite on flame retardancy, smoke suppression, and acid resistance of polypropylene/magnesium hydroxide composites // Polymer Engineering and Science. – 2022. – №62. – P. 3168–3179.Tomiak F., Rathberger K., Schöffel A. Drummer D. Expandable Graphite for Flame Retardant PA6 Applications // Polymers. – 2021. – №13. – P. 2733.Tomiak F., Rathberger K., Schöffel A. Drummer D. Expandable Graphite for Flame Retardant PA6 Applications // Polymers. – 2021. – №13. – P. 2733.Pang X., Zhang W., Meng Y., Ma M., Xu J. Effect of expansion temperature on the properties of expanded graphite and modified linear low density polyethylene // International Polymer Processing. – 2022. - № 37. – P. 271–286.Pang X., Zhang W., Meng Y., Ma M., Xu J. Effect of expansion temperature on the properties of expanded graphite and modified linear low density polyethylene // International Polymer Processing. – 2022. - № 37. – P. 271–286.Ушков В.А., Лалаян В.М., Невзоров Д.И., Ломакин С.М. О влиянии фталатных и фосфатных пластификаторов на воспламеняемость и дымообразующую способность полимерных композиционных материалов // Пожаровзрывобезопасность. – 2013. – Т. 22. – №10. – С. 25–33.Ушков В.А., Лалаян В.М., Невзоров Д.И., Ломакин С.М. О влиянии фталатных и фосфатных пластификаторов на воспламеняемость и дымообразующую способность полимерных композиционных материалов // Пожаровзрывобезопасность. – 2013. – Т. 22. – №10. – С. 25–33.Ушков В.А., Лалаян В.М., Ломакин С.М., Невзоров Д.И. Горючесть и дымообразующая способность полимерных композиционных материалов с разлагающимися минеральными наполнителями // Пожаровзрывобезопасность. – 2013. – Т. 22. – №8. – С. 15–24.Ушков В.А., Лалаян В.М., Ломакин С.М., Невзоров Д.И. Горючесть и дымообразующая способность полимерных композиционных материалов с разлагающимися минеральными наполнителями // Пожаровзрывобезопасность. – 2013. – Т. 22. – №8. – С. 15–24.Griffi n G., Bicknell A.D., Brown T.J. Studies on the Effect of Atmospheric Oxygen Content on the Thermal Resistance of Intumescent, Fire-Retardant Coatings // Journal of Fire Sciences. – 2005. – №23(4). – P. 303–328.Griffi n G., Bicknell A.D., Brown T.J. Studies on the Effect of Atmospheric Oxygen Content on the Thermal Resistance of Intumescent, Fire-Retardant Coatings // Journal of Fire Sciences. – 2005. – №23(4). – P. 303–328.Coaker A.W. Fire and fl ame retardants for PVC // Journal of Vinyl and Additive Technology. – 2003. – V.9(3). – P. 108–115.Coaker A.W. Fire and fl ame retardants for PVC // Journal of Vinyl and Additive Technology. – 2003. – V.9(3). – P. 108–115.Ушков В.А., Лалаян В.М., Невзоров Д.И., Ломакин С.М. О влиянии фталатных и фосфатных пластификаторов на воспламеняемость и дымообразующую способность полимерных композиционных материалов // Пожаровзрывобезопасность. – 2013. – Т. 22. – № 10. – С. 25–33.Ушков В.А., Лалаян В.М., Невзоров Д.И., Ломакин С.М. О влиянии фталатных и фосфатных пластификаторов на воспламеняемость и дымообразующую способность полимерных композиционных материалов // Пожаровзрывобезопасность. – 2013. – Т. 22. – № 10. – С. 25–33.Wypych G. PVC. Degradation and Stabilization. – ChemTec Publishing. – Toronto. – 2020. – P. 8, 258, 345–355.Wypych G. PVC. Degradation and Stabilization. – ChemTec Publishing. – Toronto. – 2020. – P. 8, 258, 345–355.Ахметханов Р.М., Захаров В.П., Мазина Л.А., Нафикова Р.Ф., Степанова Л.Б. Термическая и термоокислительная устойчивость поливинилхлорида, пластифицированного диоктилтерефталатом // Вестник Башкирского университета. – 2017. – Т. 22. – №4. – С. 991–995.Ахметханов Р.М., Захаров В.П., Мазина Л.А., Нафикова Р.Ф., Степанова Л.Б. Термическая и термоокислительная устойчивость поливинилхлорида, пластифицированного диоктилтерефталатом // Вестник Башкирского университета. – 2017. – Т. 22. – №4. – С. 991–995.Milner P.W. Modifi cation of PVC with NBR. In Developments in Plastics Technology – 4. Ed. by Whelan A., Goff, J.P. – Springer. – Dordrecht. – 1989. – P. 99–137.Milner P.W. Modifi cation of PVC with NBR. In Developments in Plastics Technology – 4. Ed. by Whelan A., Goff, J.P. – Springer. – Dordrecht. – 1989. – P. 99–137.Лавров Н.А., Белухичев Е.В. Полимерные смеси на основе поливинилхлорида (обзор) // Пластические массы. – 2020. – №3–4. – С. 55–59.Лавров Н.А., Белухичев Е.В. Полимерные смеси на основе поливинилхлорида (обзор) // Пластические массы. – 2020. – №3–4. – С. 55–59.Марков А.В., Тахсин А. Саки. Влияние технологических добавок на вспенивание жестких поливинилхлоридных композиций азодикарбонамидом // Вестник МИТХТ. – 2014. –Т. 9. – №3. – С. 79–85.Марков А.В., Тахсин А. Саки. Влияние технологических добавок на вспенивание жестких поливинилхлоридных композиций азодикарбонамидом // Вестник МИТХТ. – 2014. –Т. 9. – №3. – С. 79–85.Марков А.В., Тахсин А. Саки, Угличева А.Ю. Особенности вспенивания жестких поливинилхлоридных композиций азодикарбонамидом // Вестник МИТХТ. – 2013. – Т. 8.– №6. – С. 99–102.Марков А.В., Тахсин А. Саки, Угличева А.Ю. Особенности вспенивания жестких поливинилхлоридных композиций азодикарбонамидом // Вестник МИТХТ. – 2013. – Т. 8.– №6. – С. 99–102.Гуткович С.А. Влияние молекулярной массы суспензионного поливинилхлорида (ПВХ) на показатель текучести распада пластифицированной композиции // Пластические массы. – 2006. – №9. – С. 6–7.Гуткович С.А. Влияние молекулярной массы суспензионного поливинилхлорида (ПВХ) на показатель текучести распада пластифицированной композиции // Пластические массы. – 2006. – №9. – С. 6–7.