plasticnewsПластические массыPlasticheskie massy0554-2901PLASTMASSY Publishing House (Moscow)10.35164/0554-2901-2024-06-16-18plasticnews-1058Research ArticleСТРУКТУРА И СВОЙСТВАSTRUCTURE AND PROPERTIESРазработка методики измерения периода индукции окисления стабилизированного полиэтилена высокого давленияDevelopment of a method for measuring the oxidation induction period of stabilized high-pressure polyethyleneПоповаЕ. И.PopovaE. I.

Москва

Moscow

mailbox75@vniia.ruКарезинК. И.KarezinK. I.

Москва

Moscow

ЛазареваО. Л.LazarevaO. L.

Москва

Moscow

ЗотоваЕ. А.ZotovaE. A.

Москва

Moscow

НевскийР. Е.NevskiyR. E.

Москва

Moscow

СоковишинА. В.SokovishinA. V.

Москва

Moscow

Всероссийский научно-исследовательский институт автоматики им. Н.Л. ДуховаРоссияDukhov Automatics Research InstituteRussian Federation202413012025061618Copyright © Попова Е.И., Карезин К.И., Лазарева О.Л., Зотова Е.А., Невский Р.Е., Соковишин А.В., 20252025Попова Е.И., Карезин К.И., Лазарева О.Л., Зотова Е.А., Невский Р.Е., Соковишин А.В.Popova E.I., Karezin K.I., Lazareva O.L., Zotova E.A., Nevskiy R.E., Sokovishin A.V.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://www.plastics-news.ru/jour/article/view/1058

В настоящей работе осуществлен выбор граничных условий и оптимальных параметров измерения периода индукции окисления кабельного полиэтилена марки 153-01К со стабилизаторами аминного и фенольного типа. Рассчитаны зависимости ПИО от температуры выдержки в окислительной среде: в диапазоне от 180 до 220°С в среде кислорода и в диапазоне от 200 до 220°С - в среде воздуха. Для выбранных условий: окислительная среда – воздух, толщина пробы 650±100 мкм, температура выдержки +210 °С проведена статистическая оценка точности. Показано, что ОСКО разработанной методики не превышает 7%.

Choice of boundary conditions and optimal parameters for measuring of oxidation induction time of cable polyethylene grade 153-01K with amine and phenolic type antioxidants was implemented in this work. OIT dependences on holding temperature in the ranges of 180–200°С in oxygen environment and 200–220°С in the air were calculated. For selected experimental conditions (air oxidizing environment, the sample thickness of 650±100 microns and the holding temperature of 210°С) the statistical estimation of accuracy was evaluated. Relative standard deviation of developed technique was shown not to exceed 7%.

термоанализДСКпериод индукции окисленияПИОполиэтиленстабилизаторthermal analysisDSCoxidation induction timeOITpolyethyleneantioxidantReferencesISO 11357-6:2008 Plastics – Differential scanning calorimetry (DSC) – Part 6: Determination of oxidation induction time (isothermal OIT) and oxidation induction temperature (dynamic OIT).ISO 11357-6:2008 Plastics – Differential scanning calorimetry (DSC) – Part 6: Determination of oxidation induction time (isothermal OIT) and oxidation induction temperature (dynamic OIT).ASTM E 2070-03 Standard Test Method for Kinetic Parameters by DSC Using Isothermal Methods.ASTM E 2070-03 Standard Test Method for Kinetic Parameters by DSC Using Isothermal Methods.Попова Е.И., Лазарева О.Л. Опыт применения метода ДСК для контроля при производстве электронных компонентов // Труды НТК Пассивные электронные компоненты – 2011. Н. Новгород: КБ «Икар», 2011. С. 74–78.Попова Е.И., Лазарева О.Л. Опыт применения метода ДСК для контроля при производстве электронных компонентов // Труды НТК Пассивные электронные компоненты – 2011. Н. Новгород: КБ «Икар», 2011. С. 74–78.Mengjia Li Evaluation of Oxidative Behavior of Polyolefin Geosynthetics Utilizing Accelerated Aging Tests Based on Temperature and Pressure. A Thesis / Drexel University. 2005. 151 p. DOI: 10.17918/etd-467.Mengjia Li Evaluation of Oxidative Behavior of Polyolefin Geosynthetics Utilizing Accelerated Aging Tests Based on Temperature and Pressure. A Thesis / Drexel University. 2005. 151 p. DOI: 10.17918/etd-467.Bartonicek B., Hnat V., Placek V. Ageing Monitoring of Plastics used in Nuclear Power Plants by DSC // Journal of Thermal Analysis and Calorimetry. 2001. V. 64. p. 571–576. DOI:10.1023/A:1011507403569Bartonicek B., Hnat V., Placek V. Ageing Monitoring of Plastics used in Nuclear Power Plants by DSC // Journal of Thermal Analysis and Calorimetry. 2001. V. 64. p. 571–576. DOI:10.1023/A:1011507403569